| 品牌 | 杜邦 |
| 货号 | 103FHS BKB009 |
| 牌号 | 103FHS BKB009 |
| 型号 | 103FHS BKB009 |
| 品名 | PA66 |
| 外形尺寸 | 颗粒 |
| 产品用途 | 注塑 |
| 生产企业 | 杜邦 |
| 是否进口 | 是 |
DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Unreinforced Resins
非增强树脂
Zytel® 103FHS BKB009 is a heat stabilized, internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.
zytel®103FHS BKB009是一种热稳定，内部润滑聚酰胺66树脂注塑。它是快速周期和高生产率。
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66
>PA66<
|
|
Mechanical
Yield Stress
Nominal Strain at Break
Yield Strain
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
Unnotched Charpy Impact Strength
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
85(12.3)
15
4.3
3100(450)
2800(410)
5
250
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
|
ISO 75f
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
195(383)
70(158)
262(504)
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
|||
|
Flammability
Flammability Classification
0.71mm
Flammability Classification
0.71mm
Glow Wire Flammability Index
0.71mm
1.5mm
3.0mm
Glow Wire Ignition Temperature
0.71mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
IEC 60695-2-12
IEC 60695-2-13
|
℃
℃
|
V-2
V-2
850
960
960
725
725
725
|
|
Temperature Index
RTI, Electrical
0.71mm
RTI, Impact
0.71mm
1.5mm
RTI, Strength
0.71mm
1.5mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
140
95
110
115
125
|
|
Other
Density
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 294-4
|
3 3
kg/m(g/cm )
%
|
1140(1.14)
1.3
1.3
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
|||
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
280-300(535-570)
290(555)
50-90(120-190)
70(160)
2-4
80(175)
<0.20
|