DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Glass Reinforced Resins
玻璃纤维增强树脂
Zytel® 70G25HSLR NC010 is a 25% glass fiber reinforced, heat stabilized, hydrolysis resistant polyamide 66 resin for injection molding.
zytel®70G25HSLR NC010是一个25%玻璃纤维增强，热稳定，抗水解聚酰胺66树脂注塑。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-GF25
>PA66-GF25<
|
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Notched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
2
kJ/m
2
kJ/m
|
180(26.1)
3
8400(1200)
7
10
60
60
|
120(17.4)
7
6100(880)
7
11
45
80
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
|
ISO 75f
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
261(502)
252(486)
262(504)
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
CLTE, Normal
23 - 55℃(73 - 130℉)
CLTE, Parallel
23 - 55℃(73 - 130℉)
Vicat Softening Temperature
50N
|
ISO 11359-1/-2
ISO 11359-1/-2
ISO 306
|
E-4/C(E-4/F)
E-4/C(E-4/F)
℃(℉)
|
1.12(0.63)
0.33(0.18)
257(495)
|
|
|
Electrical
Relative Permittivity
1E2 Hz
Volume Resistivity
Dissipation Factor
1E2 Hz
|
IEC 60250
IEC 60093
IEC 60250
|
ohm m
E-4
|
3.6
1E13
70
|
|
|
Flammability
Flammability Classification
1.5mm
Flammability Classification
1.5mm
High Amperage Arc Ignition Resistance
1.5mm
3.0mm
Hot Wire Ignition
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
UL 746A
UL 746A
|
arcs
s
|
HB
HB
120
120
7
30
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Temperature Index
RTI, Electrical
0.71mm
1.5mm
3.0mm
RTI, Impact
1.5mm
3.0mm
RTI, Strength
1.5mm
3.0mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
105
120
120
95
95
105
110
|
|
|
Other
Density
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1320(1.32)
2
6.4
1.1
0.3
|
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
70-120(160-250)
100(210)
2-4
80(175)
<0.20
|
|