| 品牌 | 杜邦 |
| 货号 | FR7025V0F NC010 |
| 用途 | 注塑成型 |
| 牌号 | FR7025V0F NC010 |
| 型号 | FR7025V0F NC010 |
| 品名 | PA66 |
| 外形尺寸 | 颗粒 |
| 生产企业 | 杜邦 |
| 是否进口 | 是 |
DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Flame Retardant Resins
阻燃树脂
Zytel® FR7025V0F NC010 is a flame retardant polyamide 66 resin for injection molding. It does not contain elemental phosphorous, halogens or heavy metals.
zytel的®FR7025V0F NC010是具有阻燃聚酰胺66树脂注塑成型。它不含有磷元素，卤素或重金属。
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-FR(30)
>PA66-FR(30)<
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-40℃(-40℉)
23℃(73℉)
Unnotched Charpy Impact Strength
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
80(11.6)
10
3750(544)
3660(530)
3
3.7
135
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
|
ISO 75-1/-2
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
235(455)
84(183)
260(500)
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
|||
|
Electrical
CTI
|
IEC 60112
|
V
|
>600
|
|
Flammability
Flammability Classification
0.75mm
1.5mm
3.0mm
Flammability Classification
0.75mm
1.5mm
3.0mm
Glow Wire Flammability Index
1.5mm
3.0mm
Glow Wire Ignition Temperature
1.5mm
3.0mm
High Current Arc Ignition Resistance
0.75mm
1.5mm
3.0mm
High Voltage Arc Tracking Rate
0.75mm
1.5mm
3.0mm
Hot Wire Ignition
0.75mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
IEC 60695-2-12
IEC 60695-2-13
UL 746A
UL 746A
UL 746A
|
℃
℃
PLC
PLC
PLC
|
V-0
V-0
V-0
V-0
V-0
V-0
960
960
775
775
0
0
0
0
0
0
3
3
1
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
|||
|
Temperature Index
RTI, Electrical
0.75mm
1.5mm
3.0mm
RTI, Impact
0.75mm
1.5mm
3.0mm
RTI, Strength
0.75mm
1.5mm
3.0mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
130
130
130
75
75
75
85
85
85
|
|
Other
Density
Water Absorption
Immersion 24h
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1160(1.16)
1.8
1.0
0.9
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
270-290(520-555)
280(535)
50-90(120-190)
70(160)
2-4
80(175)
<0.20
|