Minlon® 22C BK086
DuPont™ Minlon® 数据
杜邦™minlon® 数据
mineral reinforced nylon resin
矿物增强尼龙树脂
Minlon ® 22C BK086 is a 38% mineral/glass reinforced, heat stabilized, black polyamide 66 resin for injection molding.
minlon®22C bk086 矿物/玻璃纤维38%增强，热稳定，黑色尼龙66树脂注塑成型。
|
Property
|
Test Method
|
Value
Units
DAM 50%RH
|
||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
PA66-(MD+GF)38
>PA66-(MD+GF)38<
|
||
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
|
MPa (kpsi)
%
MPa (kpsi)
MPa (kpsi)
2
kJ/m
|
120 (17.4)
2.5
7500 (1090)
7000 (1020)
3
|
72 (10.4)
4
5000 (725)
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10°C/min
CLTE, Normal
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 160°C (130 - 320°F)
CLTE, Parallel
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 160°C (130 - 320°F)
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
°C (°F)
°C (°F)
E-4/C (E-4/F)
E-4/C (E-4/F)
|
255 (491)
230 (446)
263 (505)
0.53 (0.29)
0.62 (0.33)
1.0 (0.56)
0.39 (0.22)
0.41 (0.23)
0.36 (0.20)
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Electrical
CTI
3.0mm
|
UL 746A
|
V
|
475
|
|
|
Flammability
Flammability Classification
0.81mm
Flammability Classification
0.81mm
High Amperage Arc Ignition Resistance
1.5mm
3.0mm
Hot Wire Ignition
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
UL 746A
UL 746A
|
arcs
s
|
HB
HB
>200
>200
117
120
|
|
|
Temperature Index
RTI, Electrical
0.81mm
RTI, Impact
0.81mm
RTI, Strength
0.81mm
|
UL 746B
UL 746B
UL 746B
|
°C
°C
°C
|
65
65
65
|
|
|
Other
Density
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 294-4
|
3 3
kg/m (g/cm )
%
|
1450 (1.45)
0.8
0.6
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Other
Mold Shrinkage
Flow, 1.6mm (0.062in)
Flow, 3.2mm (0.126in)
Flow, 6.4mm (0.25in)
Transverse, 1.6mm (0.062in)
Transverse, 3.2mm (0.126in)
Transverse, 6.4mm (0.25in)
|
|
%
|
0.5
0.6
0.6
0.8
0.8
1.0
|
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
%
|
285-305 (545-580)
295 (560)
70-120 (160-250)
100 (210)
2-4
80 (175)
<0.20
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23°C unless otherwise stated.