DuPont™ Minlon® 数据
杜邦™minlon® 数据
mineral reinforced nylon resin
矿物增强尼龙树脂
Minlon ® 22C NC010 is a 38% mineral/glass reinforced, heat stabilized polyamide 66 resin for injection molding.
minlon®22C NC010 是38%矿物/玻璃纤维增强，热稳定聚酰胺66树脂注塑成型。
|
Property
|
Test Method
|
Value
Units
DAM 50%RH
|
||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
PA66-(MD+GF)38
>PA66-(MD+GF)38<
|
||
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-40°C (-40°F)
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa (kpsi)
%
MPa (kpsi)
MPa (kpsi)
2
kJ/m
2
kJ/m
|
130 (18.9)
3.5
7500 (1090)
6500 (940)
3
3
4
40
50
|
82 (11.9)
10
5000 (725)
5000 (725)
3
4
6
35
45
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10°C/min
CLTE, Normal
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 160°C (130 - 320°F)
CLTE, Parallel
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 160°C (130 - 320°F)
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
°C (°F)
°C (°F)
E-4/C (E-4/F)
E-4/C (E-4/F)
|
255 (491)
230 (446)
263 (505)
0.53 (0.29)
0.62 (0.33)
1.0 (0.56)
0.39 (0.22)
0.41 (0.23)
0.36 (0.20)
|
|
|
Electrical
Relative Permittivity
1E2 Hz
1E6 Hz
Volume Resistivity
Dissipation Factor
1E2 Hz
1E6 Hz
Electric Strength
2.0mm
CTI
3.0mm
|
IEC 60250
IEC 60093
IEC 60250
IEC 60243-1
UL 746A
|
ohm m
E-4
kV/mm (V/mil)
V
|
4
4
1E11
100
100
20 (510)
475
|
7
4
1E7
200
500
18 (460)
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Flammability
Flammability Classification
0.81mm
Flammability Classification
0.81mm
Oxygen Index
High Amperage Arc Ignition Resistance
1.5mm
3.0mm
Hot Wire Ignition
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
ISO 4589-1/-2
UL 746A
UL 746A
|
%
arcs
s
|
HB
HB
24
>200
>200
117
120
|
|
|
Temperature Index
RTI, Electrical
0.81mm
RTI, Impact
0.81mm
RTI, Strength
0.81mm
|
UL 746B
UL 746B
UL 746B
|
°C
°C
°C
|
65
65
65
|
|
|
Other
Density
Water Absorption
Equilibrium 50%RH
Immersion 24h, 2.0mm
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m (g/cm )
%
%
|
1450 (1.45)
1.4
1.0
5.4
0.9
0.7
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Other
Mold Shrinkage
Flow, 1.6mm (0.062in)
Flow, 3.2mm (0.126in)
Flow, 6.4mm (0.25in)
Transverse, 1.6mm (0.062in)
Transverse, 3.2mm (0.126in)
Transverse, 6.4mm (0.25in)
|
|
%
|
0.6
0.7
0.8
0.8
0.9
1.1
|
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
%
|
285-305 (545-580)
295 (560)
70-120 (160-250)
100 (210)
2-4
80 (175)
<0.20
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23°C unless otherwise stated.