DuPont™ Minlon® 数据
杜邦™minlon® 数据
mineral reinforced nylon resin
矿物增强尼龙树脂
Minlon ® EFE6053 BK413 is a 40% mineral/glass reinforced, heat stabilized polyamide 66 resin for injection molding.
minlon®EFE6053 BK413是40％矿物/玻璃纤维增强，热稳定聚酰胺66树脂注塑成型。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
PA66-(GF+MD)40
>PA66-(GF+MD)40<
|
||
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa (kpsi)
%
MPa (kpsi)
MPa (kpsi)
2
kJ/m
2
kJ/m
|
160 (23.2)
2.2
10000 (1500)
9900 (1400)
4
4.5
40
45
|
97 (14.0)
4.6
6500 (940)
6
6.5
40
50
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10°C/min
CLTE, Normal
23 - 55°C (73 - 130°F)
CLTE, Parallel
23 - 55°C (73 - 130°F)
Vicat Softening Temperature
50N
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
ISO 306
|
°C (°F)
°C (°F)
E-4/C (E-4/F)
E-4/C (E-4/F)
°C (°F)
|
256 (493)
240 (464)
263 (505)
0.87 (0.48)
0.28 (0.16)
250 (482)
|
|
|
Electrical
Relative Permittivity
1E2 Hz
1E6 Hz
Dissipation Factor
1E2 Hz
1E6 Hz
Electric Strength
1.0mm
|
IEC 60250
IEC 60250
IEC 60243-1
|
E-4
kV/mm (V/mil)
|
4.9
4.8
140
130
28 (711)
|
13.9
5
5400
700
|
|
Other
Density
Ball Indention Hardness
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 2039-1
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m (g/cm )
MPa (kpsi)
%
%
|
1470 (1.47)
254 (36.8)
1.5
5
1.1
0.4
|
149 (21)
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
%
|
285-305 (545-580)
295 (560)
70-120 (160-250)
100 (210)
2-4
80 (175)
<0.20
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23°C unless otherwise stated.