| 品牌 | 杜邦 |
| 货号 | 70K20HSL NC010 |
| 牌号 | 70K20HSL NC010 |
| 型号 | 70K20HSL NC010 |
| 品名 | PA66 |
| 外形尺寸 | 颗粒 |
| 产品用途 | 注塑 |
| 生产企业 | 杜邦 |
| 是否进口 | 是 |
DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Low Wear and Friction Resins
低摩擦磨耗
Zytel® 70K20HSL NC010 is a heat stabilized PA66 resin modified with Kevlar ® aramid fiber for excellent wear resistance.
zytel®70K20HSL NC010 是热稳定尼龙66树脂改性芳纶®芳纶纤维优良的耐磨性
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-RF20
>PA66-RF20<
|
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
Unnotched Charpy Impact Strength
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
110(16.0)
5.2
5300(769)
4900(710)
6
50
|
85(12.3)
7.2
3500(510)
3300(478)
9
65
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
Vicat Softening Temperature
50N
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 306
|
℃(℉)
℃(℉)
℃(℉)
|
255(491)
222(432)
263(505)
250(482)
|
|
|
Other
Density
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1190(1.19)
2.7
6.8
1.4
0.9
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
70-120(160-250)
100(210)
2-4
80(175)
<0.20
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.