DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Toughened Resins
增韧树脂
Zytel® 80G33HS1L NC010 is a 33% glass fiber reinforced heat stabilized polyamide 66 resin with outstanding impact resistance developed using DuPont® Super Tough technology.
zytel®80G33HS1L NC010 是33%玻璃纤维增强热稳定聚酰胺66树脂，以优异的耐冲击开发利用杜邦®超级强韧技术。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-IGF33
>PA66-IGF33<
|
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Poisson's Ratio
Flexural Modulus
Notched Charpy Impact Strength
-40℃(-40℉)
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
146(21.2)
3.7
8900(1291)
0.35
7500(1090)
14
18
20
106
97
|
108(15.7)
7
6200(899)
6200(899)
18
17
28
100
98
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Normal
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
CLTE, Parallel
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
Vicat Softening Temperature
50N
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
ISO 306
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
℃(℉)
|
261(502)
246(475)
262(504)
0.96(0.53)
1.19(0.66)
1.30(0.72)
0.22(0.12)
0.15(0.08)
0.14(0.08)
245(473)
|
|
|
Electrical
Surface Resistivity
Relative Permittivity
1E6 Hz
Volume Resistivity
Dissipation Factor
1E6 Hz
CTI
3.0mm
|
IEC 60093
IEC 60250
IEC 60093
IEC 60250
UL 746A
|
ohm
ohm m
E-4
V
|
1E12
3.6
>1E13
130
400
|
4.3
1E9
600
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Flammability
Flammability Classification
0.75mm
Flammability Classification
0.75mm
High Amperage Arc Ignition Resistance
0.75mm
1.5mm
3.0mm
Hot Wire Ignition
0.75mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
UL 746A
UL 746A
|
arcs
s
|
HB
HB
150
150
120
18
103
60
|
|
|
Temperature Index
RTI, Electrical
0.75mm
RTI, Impact
0.75mm
1.5mm
RTI, Strength
0.75mm
1.5mm
3.0mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
130
65
105
85
95
105
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Other
Density
Hardness, Rockwell
Scale M
Scale R
Water Absorption
Equilibrium 50%RH
Immersion 24h
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
Mold Shrinkage
Flow, 3.2mm(0.126in)
Transverse, 3.2mm(0.126in)
|
ISO 1183
ISO 2039/2
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
%
|
1330(1.33)
70
110
1.5
0.85
4.5
0.7
0.3
0.4
1.2
|
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
50-100(120-210)
80(175)
2-4
80(175)
<0.20
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.