| 品牌 | 杜邦 |
| 货号 | ST801AW NC010 |
| 牌号 | ST801AW NC010 |
| 型号 | ST801AW NC010 |
| 品名 | PA66 |
| 外形尺寸 | 颗粒 |
| 产品用途 | 抵抗阳光直射在汽车内部应用 |
| 生产企业 | 杜邦 |
| 是否进口 | 是 |
DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Toughened Resins
增韧树脂
Zytel® ST801AW NC010 is a Super Tough, high performance polyamide 66 resin. It is UV stabilized and when appropriately colored offers the best resistance to indirect sunlight in automotive interior applications.
zytel的®ST801AW NC010是一个超级强韧，高性能聚酰胺66树脂。它是紫外线稳定和适当的颜色时，提供了 的抵抗阳光直射在汽车内部应用。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-HI
>PA66-HI<
|
|
|
Mechanical
Yield Stress
Yield Strain
Stress at Break
50mm/min
Strain at Break
50mm/min
Nominal Strain at Break
Tensile Modulus
Tensile Stress
@ 50% Strain
Flexural Modulus
Notched Charpy Impact Strength
-40℃(-40℉)
-30℃(-22℉)
-20℃(-4℉)
0℃(32℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
|
MPa(kpsi)
%
MPa(kpsi)
%
%
MPa(kpsi)
MPa(kpsi)
MPa(kpsi)
2
kJ/m
|
49(7.1)
5
45(6.5)
74
44
1900(276)
50(7.2)
1800(261)
21
23
22
36
83
|
35.5(5.1)
26.5
48(7.0)
>50
775(112)
48(7.0)
728(106)
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Mechanical
Unnotched Charpy Impact Strength
-40℃(-40℉)
-30℃(-22℉)
-20℃(-4℉)
0℃(32℉)
23℃(73℉)
|
ISO 179/1eU
|
2
kJ/m
|
240
NB
300
260
NB
|
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Normal
-30-30℃(-22-86℉)
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
CLTE, Parallel
-30-30℃(-22-86℉)
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
|
155(311)
60(140)
262(504)
1.1(0.6)
1.1(0.6)
1.2(0.7)
1.2(0.7)
1.3(0.7)
1.2(0.7)
1.4(0.8)
1.7(0.9)
|
|
|
Electrical
Surface Resistivity
Volume Resistivity
Electric Strength
Relative Permittivity
1E2 Hz
1E6 Hz
|
IEC 60093
IEC 60093
IEC 60243-1
IEC 60250
|
ohm
ohm m
kV/mm(V/mil)
|
2.7E15
2.5E14
26(660)
3.4
3.2
|
7.1E12
2.4E10
26(660)
6.0
3.5
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Electrical
Dissipation Factor
1E2 Hz
1E6 Hz
CTI
|
IEC 60250
UL 746A
|
E-4
V
|
50
110
600
|
1760
380
|
|
Flammability
Flammability Classification
0.75mm
Flammability Classification
0.75mm
High Amperage Arc Ignition Resistance
0.75mm
1.5mm
3.0mm
Hot Wire Ignition
0.75mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
UL 746A
UL 746A
|
arcs
s
|
HB
HB
150
150
150
19
28
73
|
|
|
Temperature Index
RTI, Electrical
0.75mm
RTI, Impact
0.75mm
RTI, Strength
0.75mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
125
75
85
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Other
Density
Hardness, Rockwell
Scale R
Water Absorption
Immersion 24h
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 2039/2
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1080(1.08)
110
1.17
1.8
2.0
|
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
270-300(520-570)
290(555)
50-90(120-190)
70(160)
2-4
80(175)
<0.20
|
|