DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Unreinforced Resins
非增强树脂
Zytel® 103FHS NC010 is a heat stabilized, internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.
zytel®103FHS NC010是一种热稳定，内部润滑聚酰胺66树脂注塑。它是为快速周期和高生产率。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66
>PA66<
|
|
|
Mechanical
Yield Stress
Nominal Strain at Break
Yield Strain
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
85(12.3)
20
4.5
3100(450)
2800(410)
4.5
5.5
350
NB
|
55(8.0)
>100
25
1400(200)
1300(190)
3
11
NB
NB
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Normal
23-55℃(73-130℉)
CLTE, Parallel
23-55℃(73-130℉)
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
|
200(392)
70(158)
262(504)
1.1(0.61)
1.0(0.55)
|
|
|
Electrical
CTI
CTI
3.0mm
|
IEC 60112
UL 746A
|
V
V
|
600
600
|
|
|
Flammability
Flammability Classification
0.71mm
Flammability Classification
0.71mm
Oxygen Index
Glow Wire Flammability Index
0.71mm
1.5mm
3.0mm
Glow Wire Ignition Temperature
0.71mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
ISO 4589-1/-2
IEC 60695-2-12
IEC 60695-2-13
|
%
℃
℃
|
V-2
V-2
28
850
960
960
725
725
725
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Flammability
High Amperage Arc Ignition Resistance
0.71mm
1.5mm
3.0mm
Hot Wire Ignition
0.71mm
1.5mm
3.0mm
|
UL 746A
UL 746A
|
arcs
s
|
200
>200
>200
9
11
24
|
|
|
Temperature Index
RTI, Electrical
0.71mm
RTI, Impact
0.71mm
1.5mm
RTI, Strength
0.71mm
1.5mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
|
140
95
110
115
125
|
|
|
Other
Density
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
Mold Shrinkage
Flow, 1.6mm(0.063in)
Flow, 3.2mm(0.126in)
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
%
|
1140(1.14)
2.6
8.5
1.3
1.4
1.4
1.8
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
280-300(535-570)
290(555)
50-90(120-190)
70(160)
2-4
80(175)
<0.20
|
|