DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Glass Reinforced Resins
玻璃纤维增强树脂
Zytel® 70G30HSLR NC010 is a 30% glass fiber reinforced, heat stabilized, hydrolysis resistant polyamide 66 resin for injection molding.
zytel®70G30HSLR NC010是一个30%玻璃纤维增强，热稳定，抗水解聚酰胺66树脂注塑。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-GF30
>PA66-GF30<
|
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Tensile Creep Modulus
1h
1000h
Notched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 899
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
195(28.3)
3.3
10000(1450)
10
13
70
82
|
130(18.9)
5
7200(1045)
6800(990)
5100(740)
10
15
72
92
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Normal
23-55℃(73-130℉)
CLTE, Parallel
23-55℃(73-130℉)
Vicat Softening Temperature
50N
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
ISO 306
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
℃(℉)
|
261(502)
253(487)
262(504)
1.07(0.11)
0.22(0.12)
250(482)
|
|
|
Electrical
Surface Resistivity
Relative Permittivity
1E2 Hz
1E6 Hz
Volume Resistivity
1.0mm
Dissipation Factor
1E2 Hz
1E6 Hz
Electric Strength
1.0mm
CTI
3.0mm
|
IEC 60093
IEC 60250
IEC 60093
IEC 60250
IEC 60243-1
UL 746A
|
ohm
ohm m
E-4
kV/mm(V/mil)
V
|
>1E15
4.3
4.1
>1E13
>1E15
70
150
38(964)
400
|
1E13
10.8
4.6
1E9
4600
650
32(812)
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Flammability
Flammability Classification
0.75mm
Flammability Classification
0.75mm
High Amperage Arc Ignition Resistance
0.75mm
1.5mm
3.0mm
Hot Wire Ignition
0.75mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
UL 746A
UL 746A
|
arcs
s
|
HB
HB
120
120
120
7
7
60
|
|
|
Temperature Index
RTI, Electrical
0.75mm
RTI, Impact
0.75mm
RTI, Strength
0.75mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
140
125
140
|
|
|
Other
Density
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1370(1.37)
1.9
6
1.1
0.3
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
70-120(160-250)
100(210)
2-4
80(175)
<0.20
|
|