DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Glass Reinforced Resins
玻璃纤维增强树脂
Zytel® 70G30L NC010 is a 30% glass fiber reinforced polyamide 66 resin for injection molding.
zytel®70G30L NC010是一个30%玻璃纤维增强聚酰胺66树脂注塑成型。
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-GF30
>PA66-GF30<
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Notched Charpy Impact Strength
Unnotched Charpy Impact Strength
|
ISO 527
ISO 527
ISO 527
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
2
kJ/m
2
kJ/m
|
195(28.3)
3.5
9800(1400)
13
80
|
130(18.9)
5
7200(1045)
15
93
|
Thermal
Deflection Temperature
1.80MPa
Melting Temperature
10℃/min
|
ISO 75f
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
253(487)
262(504)
|
|
Electrical
CTI
3.0mm
|
UL 746A
|
V
|
600
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Flammability
Flammability Classification
0.71mm
Flammability Classification
0.71mm
High Amperage Arc Ignition Resistance
0.71mm
1.5mm
3.0mm
Hot Wire Ignition
0.71mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
UL 746A
UL 746A
|
arcs
s
|
HB
HB
120
120
120
7
7
7
|
|
Temperature Index
RTI, Electrical
0.71mm
RTI, Impact
0.71mm
RTI, Strength
0.71mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
130
120
130
|
|
Other
Density
Molding Shrinkage
Parallel, 2.0mm
|
ISO 1183
ISO 294-4
|
3 3
kg/m(g/cm )
%
|
1370(1.37)
0.3
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
70-120(160-250)
100(210)
2-4
80(175)
<0.20
|
|