服务热线：135-3730-8655
|
 |
 |
 |
 |
 |
| 品牌 | 杜邦 |
| 货号 | 70G35HSL NC010 |
| 牌号 | 70G35HSL NC010 |
| 型号 | 70G35HSL NC010 |
| 品名 | PA66 |
| 外形尺寸 | 颗粒 |
| 产品用途 | 注塑成型 |
| 生产企业 | 杜邦 |
| 是否进口 | 是 |
DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Glass Reinforced Resins
玻璃纤维增强树脂
Zytel® 70G35HSL NC010 is a 35% glass fiber reinforced, heat stabilized polyamide 66 resin for injection molding.
zytel®70G35HSL NC010是一个35%玻璃纤维增强，热稳定聚酰胺66树脂注塑成型。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-GF35
>PA66-GF35<
|
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Notched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
2
kJ/m
2
kJ/m
|
210(30.5)
3.2
11200(1600)
10
15
80
90
|
145(21.0)
4.6
8300(1200)
10
18
75
100
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
|
ISO 75f
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
261(502)
252(486)
262(504)
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
CLTE, Normal
23-55℃(73-130℉)
CLTE, Parallel
23-55℃(73-130℉)
Vicat Softening Temperature
50N
|
ISO 11359-1/-2
ISO 11359-1/-2
ISO 306
|
E-4/C(E-4/F)
E-4/C(E-4/F)
℃(℉)
|
1(0.56)
0.2(0.11)
255(491)
|
|
|
Electrical
Surface Resistivity
Relative Permittivity
1E6 Hz
Volume Resistivity
Dissipation Factor
1E6 Hz
CTI
CTI
3.0mm
|
IEC 60093
IEC 60250
IEC 60093
IEC 60250
IEC 60112
UL 746A
|
ohm
ohm m
E-4
V
V
|
>1E15
4.1
1E15
140
400
250
|
1E13
4.7
1E9
620
|
|
Flammability
Flammability Classification
0.71mm
Flammability Classification
0.71mm
High Amperage Arc Ignition Resistance
0.71mm
1.5mm
3.0mm
Hot Wire Ignition
0.71mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
UL 746A
UL 746A
|
arcs
s
|
HB
HB
120
120
120
7
7
120
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Temperature Index
RTI, Electrical
0.71mm
RTI, Impact
0.71mm
RTI, Strength
0.71mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
140
125
140
|
|
|
Other
Density
Ball Indention Hardness
H 961/30
Hardness, Rockwell
Scale M
Scale R
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 2039-1
ISO 2039/2
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
MPa(kpsi)
%
%
|
1410(1.41)
285(41)
105
125
1.7
5.5
1.1
0.3
|
203(29)
89
117
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
70-120(160-250)
100(210)
2-4
80(175)
<0.20
|
|
返回