DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Glass Reinforced Resins
玻璃纤维增强树脂
Zytel® 70G43HSLA BK099 is a 43% glass fiber reinforced, heat stabilized, black polyamide 66 resin for injection molding.
zytel®70G43HSLA BK099是一个43％玻璃纤维增强，热稳定，黑色尼龙66树脂注塑。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-GF43
>PA66-GF43<
|
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Notched Charpy Impact Strength
Unnotched Charpy Impact Strength
Multiaxial Impact, Total Energy
4.5m/s, 2.0mm
|
ISO 527
ISO 527
ISO 527
ISO 179/1eA
ISO 179/1eU
ISO 6603-2
|
MPa(kpsi)
%
MPa(kpsi)
2
kJ/m
2
kJ/m
J(Btu)
|
225(32.6)
2.5
14000(2030)
16
90
4.4(0.004)
|
160(23.2)
3.5
11000(1595)
18
95
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
Glass Transition Temperature
10℃/min
Thermal Conductivity
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11357-1/-2
|
℃(℉)
℃(℉)
℃(℉)
2
W/m K(Btu in/h ft F)
|
258(496)
255(491)
262(504)
80(176)
0.25(1.7)
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Electrical
Volume Resistivity
Dissipation Factor
1E2 Hz
1E6 Hz
CTI
|
IEC 60093
IEC 60250
IEC 60112
|
ohm m
E-4
V
|
1E14
130
150
600
|
|
|
Flammability
Oxygen Index
|
ISO 4589-1/-2
|
%
|
24
|
|
|
Other
Density
Water Absorption
Equilibrium 50%RH, 1.0mm
Saturation, immersed, 1.0mm
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1490(1.49)
2.2
7.6
0.9
0.3
|
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
70-120(160-250)
100(210)
2-4
80(175)
<0.20
|
|