| 品牌 | 杜邦 |
| 货号 | FG70G30HSLR NC010 |
| 用途 | 品行业的零部件审议 |
| 牌号 | FG70G30HSLR NC010 |
| 型号 | FG70G30HSLR NC010 |
| 品名 | PA66 |
| 外形尺寸 | 颗粒 |
| 生产企业 | 杜邦 |
| 是否进口 | 是 |
DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Food Contact Resins
食品接触树脂
Zytel® FG70G30HSLR NC010 is a 30% glass fiber reinforced, heat stabilized, hydrolysis resistant polyamide 66 resin for injection molding. It has been developed for consideration into applications such as parts for the food industry.
zytel®FG70G30HSLR NC010是30%玻璃纤维增强，热稳定，抗水解聚酰胺66树脂注塑。它已经发展到应用如食品行业的零部件审议。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-GF30
>PA66-GF30<
|
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Tensile Creep Modulus
1h
1000h
Notched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 899
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
195(28.3)
3.3
10000(1450)
10
13
70
82
|
130(18.9)
5
7200(1045)
6800(990)
5100(740)
10
15
72
92
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Parallel
23 - 55℃(73 - 130℉)
CLTE, Normal
23 - 55℃(73 - 130℉)
Glass Transition Temperature
10℃/min
Thermal Conductivity
Specific Heat
Vicat Softening Temperature
50N
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
ISO 11357-1/-2
ISO 11357-4
ISO 306
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
℃(℉)
2
W/m K(Btu in/h ft F)
J/kg K(Btu/lb F)
℃(℉)
|
261(502)
253(487)
262(504)
0.22(0.12)
1.07(0.11)
80(176)
0.21(1.5)
2290(0.54)
250(482)
|
|
|
Other
Density
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1370(1.37)
1.9
6
1.1
0.3
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
70-120(160-250)
100(210)
2-4
80(175)
<0.20
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23℃ unless otherwise stated.
The above data are preliminary and are subject to change as additional data are developed on subsequent lots.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Zytel® are trademarks or registered trademarks of DuPont Company. Copyright© 2010