LNP Lubricomp* Olefins Compound
Enhanced wear resistance, lower friction for key r
Olefinic LNP Lubricomp compounds offer enhanced wear resistance and lower friction to key resins by combining them with internal lubricants. Glass and carbon fibers can also be included for improved strength and stiffness.
LNP™ Lubricomp™ Compound PP MX06404 塑料物性
Also known as:LNP™ Lubricomp™ Compound MFL-4034 HS LE
Product reorder name:MX06404
LNP LUBRICOMP* MX06404 is a compound based on Polypropylene resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,break | 360 | kgf/cm2 | ASTM D 638 |
| Tensile Strain,break | 1 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 59200 | kgf/cm2 | ASTM D 638 |
| Flexural Stress | 560 | kgf/cm2 | ASTM D 790 |
| Flexural Modulus | 49200 | kgf/cm2 | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 16 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 4 | cm-kgf/cm | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT,1.82 MPa,3.2mm,unannealed | 104 | ℃ | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.15 | g/cm3 | ASTM D 792 |
|
|
|||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4 | hrs |
| Melt Temperature | 225-250 | ℃ |
| Front-Zone 3 Temperature | 240-250 | ℃ |
| Middle-Zone 2 Temperature | 215-225 | ℃ |
| Rear-Zone 1 Temperature | 195-205 | ℃ |
| Mold Temperature | 30-50 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |