PP MFD02 含玻璃纤维和碳粉
- 价格： ￥15/千克
- 发布日期： 2022-03-14
- 更新日期： 2024-05-07
产品详请
| 品牌 |
液氮
|
| 货号 |
MFD02
|
| 特性级别 |
增强级|||高强度|||
|
| 牌号 |
MFD02
|
| 型号 |
MFD02
|
| 加工级别 |
注塑级|||
|
| 品名 |
PP
|
| 外形尺寸 |
颗粒
|
| 产品用途 |
注塑
|
| 用途级别 |
通用级|||
|
| 生产企业 |
液氮
|
| 是否进口 |
否
|
LNP* STAT-KON* COMPOUND
LNP STAT-KON RESIN ALL SERIES
LNP* Stat-Kon* composites contain electrically conductive additives. They and span a broad range of surface resistivity and electrical activity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding. Stat-Kon* composites offer cost-effective solutions when products must avoid static electricity buildup or discharge. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.
LNP™ STAT-KON™ Compound PP MFD02 塑料物性表
Also known as:LNP™ Stat-kon™ Compound MF-10 Product reorder name:MFD02
LNP* Stat-kon* MFD02 is a compound based on Polypropylene resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive.
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress,yield
|
280
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Stress,break
|
210
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Strain,yield
|
3.2
|
%
|
ASTM D 638
|
|
Tensile Strain,break
|
6.1
|
%
|
ASTM D 638
|
|
Tensile Modulus,50mm/min
|
28100
|
kgf/cm2
|
ASTM D 638
|
|
Flexural Modulus
|
21000
|
kgf/cm2
|
ASTM D 790
|
|
Tensile Stress,yield
|
28
|
MPa
|
ISO 527
|
|
Tensile Stress,break
|
23
|
MPa
|
ISO 527
|
|
Tensile Strain,yield
|
2.9
|
%
|
ISO 527
|
|
Tensile Strain,break
|
4.1
|
%
|
ISO 527
|
|
Tensile Modulus,1mm/min
|
2430
|
MPa
|
ISO 527
|
|
Flexural Stress
|
43
|
MPa
|
ISO 178
|
|
Flexural Modulus
|
2200
|
MPa
|
ISO 178
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact,unnotched,23℃
|
38
|
cm-kgf/cm
|
ASTM D 4812
|
|
Izod Impact,notched,23℃
|
13
|
cm-kgf/cm
|
ASTM D 256
|
|
Instrumented Impact Energy @ peak,23℃
|
170
|
cm-kgf
|
ASTM D 3763
|
|
Multiaxial Impact
|
121
|
cm-kgf
|
ISO 6603
|
|
Izod Impact,unnotched 80*10*4 +23℃
|
27
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact,notched 80*10*4 +23℃
|
15
|
kJ/m2
|
ISO 180/1A
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
HDT,0.45 MPa,3.2mm,unannealed
|
133
|
℃
|
ASTM D 648
|
|
HDT,1.82 MPa,3.2mm,unannealed
|
85
|
℃
|
ASTM D 648
|
|
CTE,-40℃ to 40℃,flow
|
1.03E-04
|
1/℃
|
ASTM E 831
|
|
CTE,-40℃ to 40℃,xflow
|
6.48E-05
|
1/℃
|
ASTM E 831
|
|
CTE,-40℃ to 40℃,flow
|
1.03E-04
|
1/℃
|
ISO 11359-2
|
|
CTE,-40℃ to 40℃,xflow
|
6.40E-05
|
1/℃
|
ISO 11359-2
|
|
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm
|
127
|
℃
|
ISO 75/Bf
|
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm
|
81
|
℃
|
ISO 75/Af
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Density
|
1.05
|
g/cm3
|
ASTM D 792
|
|
Mold Shrinkage,flow,24 hrs(5)
|
1.1-1.3
|
%
|
ASTM D 955
|
|
Mold Shrinkage,xflow,24 hrs(5)
|
1.1-1.3
|
%
|
ASTM D 955
|
|
Mold Shrinkage,flow,24 hrs(5)
|
1.2
|
%
|
ISO 294
|
|
Mold Shrinkage,xflow,24 hrs(5)
|
1.2
|
%
|
ISO 294
|
|
Density
|
1.05
|
g/cm3
|
ISO 1183
|
|
ELECTRICAL
|
Value
|
Unit
|
Standard
|
|
Surface Resistivity
|
1.E+01-1.E+03
|
Ohm
|
ASTM D 257
|
|
|
Parameter Injection Molding
|
Value
|
Unit
|
|
Drying Temperature
|
80
|
℃
|
|
Drying Time
|
4
|
hrs
|
|
Melt Temperature
|
225-250
|
℃
|
|
Front-Zone 3 Temperature
|
240-250
|
℃
|
|
Middle-Zone 2 Temperature
|
215-225
|
℃
|
|
Rear-Zone 1 Temperature
|
195-205
|
℃
|
|
Mold Temperature
|
30-50
|
℃
|
|
Back Pressure
|
0.2-0.3
|
MPa
|
|
Screw Speed
|
30-60
|
rpm
|