您当前的位置: 网站首页 > 产品展厅 >PP PE >PP MX01767C 含专有填料 清洁复合系统

产品介绍

PP MX01767C 含专有填料 清洁复合系统
物品单位 价格 品牌
千克 18 液氮
  • 货号:MX01767C
  • 发布日期: 2022-03-14
  • 更新日期: 2022-03-14
产品详细说明
品牌 液氮
货号 MX01767C
特性级别 增强级|||高强度|||
牌号 MX01767C
型号 MX01767C
加工级别 注塑级|||
品名 PP
外形尺寸 颗粒
产品用途 注塑
用途级别 通用级|||
生产企业 液氮
是否进口

LNP* STAT-KON* COMPOUND
LNP STAT-KON RESIN ALL SERIES
LNP* Stat-Kon* composites contain electrically conductive additives. They and span a broad range of surface resistivity and electrical activity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding. Stat-Kon* composites offer cost-effective solutions when products must avoid static electricity buildup or discharge. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.

LNP™ STAT-KON™ Compound PP MX01767C 塑料物性表

Also known as:LNP™Stat-kon™Compound PDX-M-01767 CCS Product reorder name:MX01767C
LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 320 kgf/cm2 ASTM D 638
Tensile Stress,brk,Type I,5mm/min 200 kgf/cm2 ASTM D 638
Tensile Strain,yld,Type I,5mm/min 7.5 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 25.5 % ASTM D 638
Tensile Modulus,5mm/min 18000 kgf/cm2 ASTM D 638
Flexural Modulus,1.3mm/min,50mm span 15100 kgf/cm2 ASTM D 790
Tensile Stress,yield,5mm/min 31 MPa ISO 527
Tensile Stress,break,5mm/min 22 MPa ISO 527
Tensile Strain,yield,5mm/min 6.6 % ISO 527
Tensile Strain,break,5mm/min 18 % ISO 527
Tensile Modulus,1mm/min 1570 MPa ISO 527
Flexural Stress 35 MPa ISO 178
Flexural Modulus,2mm/min 1510 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 149 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 13 cm-kgf/cm ASTM D 256
Multiaxial Impact 326 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 377 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 141 kJ/m2 ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 9 kJ/m2 ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 95 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 53 ASTM D 648
CTE,-40℃ to 40℃,flow 9.20E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 9.50E-05 1/℃ ASTM E 831
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 89 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 52 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 0.98 - ASTM D 792
Density 0.98 g/cm3 ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.02 % ASTM D 570
Mold Shrinkage,flow(5) 1 % SABIC Method
Mold Shrinkage,xflow(5) 2 % SABIC Method
Moisture Absorption(23℃/50% RH) 0.01 % ISO 62
ELECTRICAL Value Unit Standard
Surface Resistivity 3.00E+00 Ohm ASTM D 257

Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Melt Temperature 225-250
Front-Zone 3 Temperature 240-250
Middle-Zone 2 Temperature 215-225
Rear-Zone 1 Temperature 195-205
Mold Temperature 30-50
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm