服务热线：13537308655
|
| 品牌 | 普立万 |
| 货号 | PPR-30G Black |
| 用途 | 注塑 |
| 特性级别 | 耐高温||| |
| 牌号 | PPR-30G Black |
| 型号 | PPR-30G Black |
| 加工级别 | 注塑级||| |
| 品名 | PP |
| 外形尺寸 | 颗粒 |
| 用途级别 | 填充级|||汽车部件||| |
| 生产企业 | 普立万 |
| 是否进口 |
PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc.
Information provided by PolyOne
PolyOne Maxxam™ PPR-30G Black Polypropylene Homopolymer (PP Homopolymer) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| 线性成型收缩率,Flow | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | ASTM D955 |
| 熔体流动速率 | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 446 °F | Procedure A; ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | 82.0 MPa | 11900 psi | Type I, 51 mm/min; ASTM D638 |
| 伸长率 (断裂) | 9.0 % | 9.0 % | Type I, 51 mm/min; ASTM D638 |
| 弯曲强度 | 115 MPa | 16700 psi | ASTM D790 |
| 弯曲模量 | 5.03 GPa | 730 ksi | ASTM D790 |
| 悬壁梁缺口冲击强度 | 0.800 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 1.50 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A |
| 悬壁梁无缺口冲击强度 | 3.40 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 6.37 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.46 MPa) | 162 °C @Thickness 3.18 mm | 324 °F @Thickness 0.125 in | Unannealed; ASTM D648 |
| 可燃性(UL94) | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | ALL; UL 94 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 模具温度 | 16.0 - 50.0 °C | 60.8 - 122 °F |
| 材料描述 | 测试方法 | |
|---|---|---|
| 外观 | Black | |
| 特性 | Chemically Coupled | |
| General Purpose | ||
| Homopolymer | ||
| Filler / Reinforcement | Glass Fiber Reinforcement | |
| Unspecified FillerReinfor., 30% Filler by Weight | ||
| 形式 | Pellets | |
| 通用材料 | PP Homopolymer | |
| 通用名 | Polypropylene Homopolymer (PP Homopolymer) | |
| 加工方法 | Injection Molding | |
| 供货地区 | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| 用途 | Automotive Applications | |
| Construction Applications | ||
| Consumer Applications | ||
| General Purpose | ||
| Industrial Applications |