| 品牌 | 道康宁 |
| 货号 | 3040-70A |
| 牌号 | 3040-70A |
| 型号 | 3040-70A |
| 品名 | 其它热塑性弹性体 |
| 外形尺寸 | 颗粒 |
| 产品用途 | 表带料 |
| 生产企业 | 道康宁 |
| 是否进口 | 是 |
代理道康宁TPSiV 3040-70A BLK 25349
Density | 1.17 | g/cm? | ISO 1183 |
Spiral Flow 2 | 17.0 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
Shore Hardness (Shore A) | 70 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
Tensile Stress - Across Flow 3 (100% Strain) | 3.30 | MPa | ISO 37 |
Tensile Stress - Across Flow 3 (Break) | 13.0 | MPa | ISO 37 |
Tensile Elongation - Across Flow 3 (Break) | 590 | % | ISO 37 |
Tear Strength - Across Flow | 49 | kN/m | ISO 34-1 |
| Injection | Nominal Value | Unit | |
Drying Temperature - Desiccant Dryer | 80 to 100 | °C | |
Drying Time | 3.0 to 6.0 | hr | |
Suggested Max Moisture | <0.030 | % | |
Rear Temperature | 170 to 180 | °C | |
Middle Temperature | 185 to 195 | °C | |
Front Temperature | 195 to 200 | °C | |
Nozzle Temperature | 200 to 210 | °C | |
Mold Temperature | 10 to 40 | °C | |
Back Pressure | 0.700 to 1.40 | MPa | |
Screw Speed | 100 to 150 | rpm | |
Vent Depth | 0.013 to 0.025 | mm |
硅基热塑性硫化胶（ TPSiV）是道康宁公司开发的世界上以硫化硅橡胶颗粒在热塑性基材上形成的热塑 性有机硅弹
性体，该系列有机硅弹性体拥有 13 项专利技术。通过有机硅的表面富集性和憎水性，不仅拓展了热塑性弹性体和热塑
性硫化胶的性能，使得其具有优良的抗高温性能，高温时的低拉伸性和压缩性以及良好的
耐磨性、抗水解性和耐化学（包括燃料和油性），同时，相对于普通热塑性弹性体而言，有机硅弹性体
具有更加优异的包覆性和独特的人体美学触感，并且可以回收使用、绿色环保，目前广泛应用于消费电子、化妆品、食品、
汽车、运动休闲等各个行业。
起源及结构特点
TPSiV 是热塑性有机硅弹性体（ Thermo Plastic Silicone Vulcanizate ）的简称及注册商标。它是应用道康
宁所*的具有 13 项专利的动态硫化交联技术将充分硫化的硅橡胶微粒，均匀分散在热塑性材料的连续相中
所形成的一种稳定的 TPV 高分子合金。与高分子合成方法制备的热塑性弹性体 TPE 相比， TPSiV 具有以下特点：
（1）具有特殊的海—岛相态结构，其中微小的硅橡胶粒子呈分散相存在，而热塑性基体则以连续相包覆在硅