DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Glass Reinforced Resins
玻璃纤维增强树脂
Zytel® 70G13HS1L BK031 is a 13% glass fiber reinforced, heat stabilized, black polyamide 66 resin for injection molding.
zytel®70G13HS1L BK031 是一个13%玻璃纤维增强，热稳定，黑色尼龙66树脂注塑。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-GF13
>PA66-GF13<
|
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Flexural Modulus
Flexural Strength
Notched Charpy Impact Strength
-40℃(-40℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 178
ISO 179/1eA
|
MPa(kpsi)
%
MPa(kpsi)
MPa(kpsi)
MPa(kpsi)
2
kJ/m
|
120(17.4)
2.7
5500(800)
4900(710)
190(27.6)
4.5
5
|
75(10.8)
12
3500(508)
100(14.5)
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
|
ISO 75f
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
258(496)
238(460)
262(504)
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
CLTE, Normal
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
CLTE, Parallel
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
|
ISO 11359-1/-2
ISO 11359-1/-2
|
E-4/C(E-4/F)
E-4/C(E-4/F)
|
0.77(0.43)
0.96(0.53)
1.58(0.88)
0.42(0.23)
0.40(0.22)
0.27(0.15)
|
|
|
Electrical
CTI
3.0mm
|
UL 746A
|
V
|
>600
|
|
|
Flammability
Flammability Classification
0.71mm
High Amperage Arc Ignition Resistance
0.71mm
Hot Wire Ignition
0.71mm
1.5mm
3.0mm
|
UL94
UL 746A
UL 746A
|
arcs
s
|
HB
>200
12
7
8
|
|
|
Temperature Index
RTI, Electrical
0.71mm
RTI, Impact
0.71mm
RTI, Strength
0.71mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
140
125
140
|
|
|
Other
Density
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 294-4
|
3 3
kg/m(g/cm )
%
|
1230(1.23)
1.0
0.5
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305(545-580)
295(565)
70-120(160-250)
100(210)
2-4
80(175)
<0.20
|
|